  The rubber magnet material itself has high plasticity, and its finished product has good flexibility, therefore, the complicated and thin-walled product with arbitrary shape can be prepared. Moreover, this product has good consistency, high dimensional accuracy, good impact shock resistance, difficult breaking, and small proportion of magnet, thereby facilitating the light weight of device and complete machine. It can be made into the magnet with fully radical (fully radiated) orientation, can be mounted on PVC, PP synthetic paper, double faced adhesive tape and others, and can be made into various products.



  • Introduction
  • Physical property
  • Diagram
  • Magnetic property
  • Production process
  • ●The finished product is manufactured by squeezing or rolling.

    ●As the material itself has high plasticity, the finished products or semi-finished products can be used for randomly cutting, punching, lengthwise cutting and mounting other goods.

    ●It is difficult to demagnetize, and has good corrosion prevention, low price, rich resources, and high-cost/performance proportion.

  • Tensile Strength (Mpa) >2.5 >2.5 >2.5 >2.5 >2.5 >2.5 >2.5 >2.5 >2.5
    Elongation(%) >20 >20 >20 >20 >20 >20 >20 >20 >20
    Hardness(Shore D) 40~65 40~65 40~65 40~65 40~65 40~65 40~65 40~65 40~65
    Density (g/m3) 3.6~3.8 3.6~3.8 3.6~3.8 3.6~3.8 3.6~3.8 3.6~3.8 3.6~3.8 3.6~3.8 3.6~3.8
    Weight reductio by heat (%) <2.0 <2.0 <2.0 <2.0 <2.0 <2.0 <2.0 <2.0 <2.0
    Temperature range (℃) -40~100 -40~100 -40~100 -40~100 -40~100 -40~100 -40~100 -40~100 -40~100
  •  
  • category Industry Standard SJ/T 10410 Br>= Hcb>= Hcj>= BHmax>=
    mT Gs KA/m Oe KA/m Oe KJ/m3 MGOe
    Homosexual extrusion >YN4T,<YN10 170 1700 104 1300 155 1950 5.18 0.65
    Homogeneous calendering >YN4T,<YN10 185 1850 112 1400 147 1850 5.18 0.8
    Semi-exclusive extrusion >YN4T,<YN10 180 1800 115 1450 167 2100 5.97 0.75
    Semiperiodic calendering >YN4T,<YN10 200 2000 119 1500 151 1900 6.77 0.85
    The opposite sex is extruded >YN4T,<YN10 210 2100 143 1800 199 2550 8.76 1.1
    Alienation YN11 245 2450 167 2100 199 2500 11.15 1.4
    High performance heterosexual extrusion YN10 225 2250 155 1950 223 3000 9.95 1.25
    High performance anisotropy YN13 260 2600 179 2250 207 2600 13.14 1.65
    Remarks 1. Above for the magnetic parameters of automatic test instrument measurements.
    2. Unit conversion: 1T=103mT=104Gs; 1KA/m=4πOe; 1KJ/m3=4πx10-2MGOe.
  •  
  •  